PC 10GF
CROW logo
10 - 30% Glass Fiber filled Polycarbonate
 

Thermo-Physical Properties

PROPERTY UNIT VALUE / RANGE 
Melting Point °C 
Density g mL-1 1.27 - 1.42
Coefficient of Thermal Expansion x 10-5cm / (cm °C) 0.35 - 0.65
Heat Deflection Temperature, 0.5 MPa °C 141 - 149
Heat Deflection Temperature, 1.8 MPa °C 134 - 141
Thermal ConductivityW / mK  
Shore Hardness,  R & M Scalen/a  
    
 

Mechanical Properties at 23 °C

PROPERTY UNITVALUE / RANGE
Tensile Strength, Yield at 23 C MPa 82 - 99
Tensile Strength, Break at 23 C MPa 85 - 105
Elongation, Yield % 2.5 - 4.6
Elongation, Break % 2.2 - 15
Tensile Modulus at 23 CMPa 3800 - 6000
Flexural Strength, Yield MPa  
Flexural Modulus  MPa 3600 - 5500
Compressive Strength MPa 
Izod Notched kJ / m2 8 - 12
Izod Unnotched kJ / m2  
 

Electrical Properties

PROPERTY UNITVALUE / RANGE
Volume Resistivity
Ohm-cm 
 Dielectric Strength V/mm x 104 3.6
Dielectric Constant @ 1 MHz n/a 3.2 - 3.5
Dissipation Factor @ 1 MHz n/a, x 10-4  
 

Other Properties

PROPERTY UNITVALUE / RANGE
Processing Temperature
°C300
Linear Mold Shrinkage cm/cm  
Continuous Service Temperature °C  
Water Absorption, 24 hr. Immersion% 0.24
back to top